700ZR is two component polyamide cured high zinc contains, zinc rich epoxy primer. It provides very good corrosion protection as part of a complete coating system. To be used as primer in atmospheric environments.
Indopoxy 700ZR is recommended for structural steel, tanks, pipe lines to be exposed to highly corrosive environments like C5I or C5M (ISO12944-2) in refineries, power plants, bridges, buildings, mining equipment and general structural steel like electrical transfomers etc. Recommended as a primer for coating systems where extended durability is required.
Colour
Grey
Finish
Matt
Soild by Volume
55 ± 3%
Supply Weight (Kg/ Ltr)
2.50±0.05
Flash Point
29° C
Dry Heat Resistance
Intermittent : 160°C, Continuous : 130°C
Shelf Life
12 months
Recommended film thickness per coat
Dry Film Thickness
30-70μ in single coat
Wet Film Thickness
55-120μ in single coat
Therotical Coverage Rate
14 sq.mt / lit at recommended DFT of 40μ
All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.
New steel : Abrasive blasting to Sa 2½ (ISO 8501-1:2007). For temporary protection, if required, use a suitable shopprimer. All damage of shopprimer and contamination from storage and fabrication should be thoroughly cleaned prior to final painting.
Shop Primed : Indopoxy 700ZR is suitable for application to steelwork freshly coated with zinc silicate shop primers ONLY. If the zinc silicate shop primer shows extensive or widely scattered breakdown, or excessive zinc corrosion, overall sweep blasting is a must. Other than zinc silicate shop primed surfaces are not suitable for overcoating and will require complete removal by abrasive blast cleaning.
Application Method
Airless Spray/ Spray/ Brush/ Roller
Mixing Ratio
3 Part (Base) : 1 Part (Hardener)
Pot Life
Eight Hours at 30°C
Thinner and Cleaner
Indopoxy Epoxy Thinner (IK.1501)
Airless Nozzle Orifice
0.43 - 0.53mm
Nozzle Pressure
176 kg/cm² or 2500 psi