Indoauto 440MIO

/ Intermediates / Modified Alkyd / Indoauto 440MIO

Modified Alkyd

High Build Zinc Phosphate MIO Coating

This is a one component oxidatively drying modified alkyd coating. It is a fast drying, high build, zinc phosphate and micaceous iron oxide pigmented product. Can be used as primer or mid coat in atmospheric environments. Suitable for properly prepared carbon steel, aluminium and wooden substrates.

Recommended Use

440MIO is recommended as primer or mid coat over structural steel, forging and casting components, heavy machineries components, pipelines etc to provide barrier and corrosion protection. Recommended only in mild corrosive atmosphere.

  • Colour

    Reddish Grey

  • Finish

    Matt

  • Soild by Volume

    58 ± 3%

  • Supply Weight (Kg/ Ltr)

    1.40±0.05

  • Flash Point

    32° C

  • Dry Heat Resistance

    Intermittent : 140°C, Continuous : 120°C

  • Shelf Life

    12 months

Film Thickness

Recommended film thickness per coat

  • Dry Film Thicknes

    50-80μ in single

  • Wet Film Thickness

    80-135μ in single

  • Therotical Coverage Rate

    10.00 sq.mt / lit at recommended DFT of 60μ

All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.


Steel : Abrasive blast clean to a minimum of Sa2½ (ISO 8501-1:2007). Surface defects revealed by the blast cleaning process should be ground, filled, or treated in the appropriate manner. A surface profile of 30-40 microns is recommended.


Maintenance : The surface should be hand or machine abraded or hand abrasive pads to impart a scratch pattern to the surface and to remove all polish from the surface. Else abrasive sweep blast to a standard similar to ISO 8501-1:2007 Sa1 to create a surface profile.


Primed Surface : Already primed surface should be dry and free from all contamination. Remove all loose or flaking coatings, loose rust or other surface contamination using hand or power tool methods, to achieve SSPC SP2 or SSPC SP3 on bare areas.


Wood : Clean and dry surface. Surface contamination is to be removed by detergents and fresh water cleaning.

  • Application Method

    Spray/ Airless Spray/Brush/ Roller

  • Mixing Ration

    One Component Coating

  • Thinner and Cleaner

    Indokote Thinner (IK.707)

  • Airless Nozzle Orifice

    0.48 - 0.53mm

  • Nozzle Pressure

    141 kg/cm² or 2000 psi