Indothane 1067HS

/ Finishes / Polyurethane / Indothane 1067HS

Polyurethane

Acrylic Polyurethane High Solid High Protective Finish

Two component Acrylic Polyurethane based, Aliphatic Isocyanate cured High Performance, High Solid finish to provide excellent Gloss and Colour retention. Indothane 1067HS is suitable to both new fabrication and maintenance and is highly recommended finish coat in Chemical/ Extreme environments.

Recommended Use

This product is recommended as topcoat over Epoxy or PU based anti corrosive primed surface in a wide range of aggressive environments. It is recommended for Refinaries, Chemical Plants, Offshore Structures, Power Plants, Petrochemical complexes, Bridges and Heavy Infrastructure Projects. Indothane 1067HS exhibits superior application properties, environmental durability and chemical resistance.

  • Colour

    Any IS/ RAL/ Custom Shades

  • Finish

    Glossy (70-85GU)

  • Soild by Volume

    64 ± 2%

  • Supply Weight (Kg/ Ltr)

    1.20±0.05

  • Flash Point

    29° C

  • Dry Heat Resistance

    Intermittent : 120°C, Continuous : 100°C

  • Shelf Life

    12 months

Film Thickness

Recommended film thickness per coat

  • Dry Film Thickness

    40-80μ in single coat

  • Wet Film Thickness

    60-120μ in single coat

  • Therotical Coverage Rate

    13.00 sq.mt / lit at recommended DFT of 50μ

All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.


Primed Surface : Indothane 1067HS should be always be applied over anti corrosive primed surface. For final smooth finish, proper sanding of already coated primer is recommended. Existing system should be dry and free from loose paint, salt, grease and other contaminants prior to overcoating.


Maintenance : Area of damage or rework etc should be prepared as per specified standards, either by power tool cleaning or other means. A patch primer should be applied before application of Indothane 1067HS for desired performance of the product.

  • Application Method

    Spray/ Airless Spray/Brush/ Roller

  • Mixing Ratio

    9 Part (Base) : 1 Part (Hardener)

  • Pot Life

    Three Hours at 30°C

  • Thinner and Cleaner

    Indothane PU Thinner (IK.1705)

  • Airless Nozzle Orifice

    0.38 - 0.53mm

  • Nozzle Pressure

    155 kg/cm² or 2200 psi