Two component Acrylic Polyurethane based, Aliphatic Isocyanate cured High Performance, medium Solid finish to provide excellent Gloss and Colour retention. To be used as topcoat in atmospheric environments.
This product is recommended as topcoat over Epoxy or PU based anti corrosive primed surface in a wide range of aggressive environments. It is recommended for Electrical Transformers, Radiators, Structures, Heavy Machineries, Process industries, pharmaceutical industries etc to exhibits excellent gloss, asthetics and environmental durability.
Colour
Any IS/ RAL/ Custom Shades
Finish
Glossy (80-95GU at 60° angle)
Soild by Volume
48 ± 2%
Supply Weight (Kg/ Ltr)
1.10±0.05
Flash Point
26° C
Dry Heat Resistance
Intermittent : 120°C, Continuous : 100°C
Shelf Life
12 months
Recommended film thickness per coat
Dry Film Thickness
30-50μ in single coat
Wet Film Thickness
60-100μ in single coat
Therotical Coverage Rate
16.50 sq.mt / lit at recommended DFT of 30μ
All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.
Primed Surface : Indothane 1033 should be always be applied over anti corrosive primed surface. For final smooth finish, proper sanding of already coated primer is recommended. Existing system should be dry and free from loose paint, salt, grease and other contaminants prior to overcoating.
Maintenance : Area of damage or rework etc should be prepared as per specified standards, either by power tool cleaning or other means. A patch primer should be applied before application of Indothane 1033 for desired performance of the product.
Application Method
Conventional Spray/ Airless Spray/Brush/ Roller
Mixing Ratio
4 Part (Base) : 1 Part (Hardener)
Pot Life
Three Hours at 30°C
Thinner and Cleaner
Indothane PU Thinner (IK.1705)
Airless Nozzle Orifice
0.38 - 0.45mm
Nozzle Pressure
155 kg/cm² or 2200 psi