Two component EPOXY based Polymide cured chemical resistance, high build, high performance intermediate or finish with excellent chemical and abrasion resistance.
Recommended to use as part of a high performance coating system to provide an anti-corrosive barrier in areas where aggressive corrosion conditions prevail.
Indopoxy 5070HB is can be widely used in both new construction and industrial maintenance on offshore structures, chemical plants, power stations and pulp and paper plants on both steel and concrete.
Colour
Most IS/ RAL/ Custom Shades
Finish
Semi Glossy (30-50GU at 60° angle)
Soild by Volume
62 ± 2%
Supply Weight (Kg/ Ltr)
1.45±0.05
Flash Point
26° C
Dry Heat Resistance
Intermittent : 120°C, Continuous : 100°C
Shelf Life
12 months
Recommended film thickness per coat
Dry Film Thickness
80-120μ in single coat
Wet Film Thickness
130-190μ in single coat
Therotical Coverage Rate
7.50 sq.mt / lit at recommended DFT of 80μ
All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.
Primed Surface : The primed surface should be dry and free from all contamination and Indopoxy 5070 should be applied within the overcoating intervals specified in primer TDS. Area of damaged primer or rework etc should be prepared as per specified standards, either by power tool cleaning or other means.
Maintenance : Remove oil and grease, salts and other contaminants by high pressure fresh water cleaning. Clean damaged areas thoroughly by power tool cleaning to St 3 (ISO 8501-1:2007) (minor areas) or by abrasive blasting to min. Sa 2, preferably to Sa 2½ (ISO 8501-1:2007). A patch primer should be applied before application of Indopoxy 5070 for desired performance of the product.
Concrete : Indopoxy 5070 is suitable to apply over concrete surfaces. Concrete should be cured for a minimum of 30 days prior to coating. The moisture content of the concrete should be below 5%. All surfaces should be clean, dry and free from curing compounds, release agents, trowelling compounds, surface hardeners, efflorescence, grease, oil, dirt, old coatings. All poured and precast concrete must also be sweep blasted (preferred) or acid etched to remove laitence. Priming should be carried out using Indopoxy 5070HB or Indopoxy 5070 at low viscosity to fill pores surface before final coating.
Application Method
Conventional Spray/ Airless Spray/Brush/ Roller
Mixing Ratio
4 Part (Base) : 1 Part (Hardener)
Pot Life
Three Hours at 30°C
Thinner and Cleaner
Indothane Epoxy Thinner (IK.1501)
Airless Nozzle Orifice
0.45 - 0.58mm
Nozzle Pressure
176 kg/cm² or 2500 psi
Download Brochure