Indoauto 4400G

/ DTM (Primer-Finishes) / Modified Alkyd / Indoauto 4400G

Modified Alkyd

High Solid Modified Alkyd based DTM (Direct-to-Metal) Finish

A single component, high solids, fast curing, modified alkyd based primer cum finish pigmented with zinc phosphate to provide added anti corrosive performance and a decorative finish in a single coat.

Recommended Use

Specifically designed for use as a single or two coat direct to metal coating system to protect construction and mining heavy machinery, agricultural equipment, railcars, transportation vehicles, material handling and lifting equipment, pumps, valves, gear units and other small motors and machinery.
Indoauto 4400G is particularly suited for use as a rapid drying system for fast handling times and maximising the production throughput.

  • Colour

    Custom Shades on request

  • Finish

    High Glossy (85+ Gloss Units at 60° angle)

  • Soild by Volume

    59 ± 3%

  • Supply Weight (Kg/ Ltr)

    1.20±0.05

  • Flash Point

    30° C

  • Dry Heat Resistance

    Intermittent : 80°C, Continuous: 60°C

  • Shelf Life

    12 months

Film Thickness

Recommended film thickness per coat

  • Dry Film Thickness

    60-100μ in single coat

  • Wet Film Thickness

    100-165μ in single coat

  • Therotical Coverage Rate

    10.00 sq.mt / lit at recommended DFT of 60μ

All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning. This product is suitable for use over phosphate washed steel.


Primed Surface : The primed surface should be dry and free from all contamination and Indoauto 4400G should be applied within the overcoating intervals specified in primer TDS. Area of damaged primer or rework etc should be prepared as per specified standards, either by power tool cleaning or other means.


Steel : Abrasive blast clean to a minimum of Sa2½ (ISO 8501-1:2007). Surface defects revealed by the blast cleaning process should be ground, filled, or treated in the appropriate manner. A surface profile of 30-40 microns is recommended.


Stainless Steel : Dirt and oils should be removed by solvent cleaning or other suitable cleaner followed by a thorough water rinsing. Sand or abrasive sweep blast to a standard similar to ISO 8501-1:2007 Sa1 to create a surface profile.

  • Application Method

    Spray/ Airless Spray/Brush/ Roller

  • Mixing Ration

    One Component Coating

  • Pot Life

    NA

  • Thinner and Cleaner

    Indokote Thinner (IK.707)

  • Airless Nozzle Orifice

    0.33 - 0.45mm

  • Nozzle Pressure

    155 kg/cm² or 2200 psi

quick inquiry