Indopoxy 5100

/ DTM (Primer-Finishes) / Epoxy / Indopoxy 5100

Epoxy

Epoxy High Performance DTM (Direct-to-Metal) Finish

Two component EPOXY based High Solid Fast Curing chemical resistance Direct-to-Metal Finish. Indopoxy 5100 contains Zinc Phsophate as Anti Corrosive Pigment and has excellent performance when exposed to moderate corrosive/ industrial environment.

Recommended Use

It is recommended as finsh coat on Structures, Equipments, Valves, Pipe Lines, Transformer Tanks, Storage Tanks etc in Infrastructure projects, Bridges, Steel Plants, Heavy Electrical Industries or in General Industrial applications. Indopoxy 5100 provides anti corrosive barrier and chemical/ oil spillage resistance along with slip and abrasion resistance. Also recommended as primer or intermediate coat in 3 coat high performance system.

  • Colour

    Any IS/ RAL/ Custom Shades

  • Finish

    Semi Glossy to Glossy

  • Soild by Volume

    67 ± 3%

  • Supply Weight (Kg/ Ltr)

    1.40±0.05

  • Flash Point

    26° C

  • Dry Heat Resistance

    Intermittent : 120°C, Continuous : 120°C

  • Shelf Life

    12 months

Film Thickness

Recommended film thickness per coat

  • Dry Film Thickness

    50-150μ in single coat

  • Wet Film Thickness

    75-210μ in single coat

  • Therotical Coverage Rate

    8.50 sq.mt / lit at recommended DFT of 80μ

All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.


Primed Surface : The primed surface should be dry and free from all contamination and Indopoxy 5100 should be applied within the overcoating intervals specified in primer TDS. Area of damaged primer or rework etc should be prepared as per specified standards, either by power tool cleaning or other means.


New steel : Abrasive blasting to Sa 2½ (ISO 8501-1:2007). For temporary protection, if required, use a suitable shopprimer. All damage of shopprimer and contamination from storage and fabrication should be thoroughly cleaned prior to final painting.


Maintenance : Remove oil and grease etc. thoroughly with suitable detergent. Remove salts and other contaminants by high pressure fresh water cleaning. Clean damaged areas thoroughly by power tool cleaning to St 3 (ISO 8501-1:2007) (minor areas) or by abrasive blasting to min. Sa 2, preferably to Sa 2½ (ISO 8501-1:2007). Improved surface preparation will improve the performance of the product.


Stainless steel : To be abrasive blast cleaned to a uniform, sharp, dense profile (ISO Comparator Medium (G), corresponding to Rz minimum 50 micron. Any salts, grease, oil, etc. to be removed before abrasive blasting is commenced.

  • Application Method

    Spray/ Airless Spray/Brush/ Roller

  • Mixing Ratio

    4 Part (Base) : 1 Part (Hardener)

  • Pot Life

    Three Hours at 30°C

  • Thinner and Cleaner

    Indopoxy Epoxy Thinner (IK.1501)

  • Airless Nozzle Orifice

    0.43 - 0.58mm

  • Nozzle Pressure

    155 kg/cm² or 2200 psi