Two component Aliphatic Acrylic Polyurethane based High Gloss Clear finish to provide excellent Gloss and Gloss retention. Indothane 1070C is suitable to Automotive Refinish in wet-to-wet application and for High Quality Wood Finish equally.
This product is recommended as final coat over finely prepared pigmented topcoats to provide high quality gloss and protection from extreme weather. It provides good chemical and physical resistance and is also has non yellowing resistance. Specially recommended in Automotive refinish system for high gloss of metallic and solid shades over Sheet Metal, ABS and Alloys. 1070C is also recommended as weather protective coating for wood and wood flooring.
Colour
Clear (Transperent)
Finish
High Gloss (90GU+ at 60° angle)
Soild by Volume
45 ± 2%
Supply Weight (Kg/ Ltr)
1.01±0.05
Flash Point
29° C
Dry Heat Resistance
Intermittent : 100°C, Continuous : 80°C
Shelf Life
12 months
Recommended film thickness per coat
Dry Film Thickness
20-40μ in single coat
Wet Film Thickness
45-90μ in single coat
Therotical Coverage Rate
15.00 sq.mt / lit at recommended DFT of 30μ
All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.
ABS Components : Should be applied after proper sanding of already coated surface by emery papaer 320/ 400 for proper adhesion. Existing system should be dry and free from loose paint, salt, grease and other contaminants prior to overcoating.
New steel : Abrasive blasting to Sa 2½ (ISO 8501-1:2007) or 7 tank process of phosphating is a must for base coat adhesion. All uneven surface and contamination from handling/ storage etc should be thoroughly cleaned prior to final painting.
Maintenance : Remove dirt, oil and grease etc. thoroughly with suitable cleaner. Remove salts and other contaminants by isopropyl Alcohal cleaning. Clean surface areas thoroughly by emery paper or by abrasive blasting to min. Sa 2, preferably to Sa 2½ (ISO 8501-1:2007). Improved surface preparation will improve the performance of the product.
Wood : To be sanded by power grinding or emery paper to a uniform, sharp, smooth profile corresponding to Rz minimum 50 micron. Any dirt, grease, oil, etc. to be removed before application is commenced.
Application Method
Spray/ Airless Spray/Brush/ Roller
Mixing Ratio
4 Part (Base) : 1 Part (Hardener)
Pot Life
Three Hours at 30°C
Thinner and Cleaner
Indothane PU Thinner (IK.1705)
Airless Nozzle Orifice
0.38 - 0.53mm
Nozzle Pressure
155 kg/cm² or 2200 psi