A fast drying, high performance universal anti corrosive primer in single component range of products, pigmented with Zinc Phosphate as corrosion inhibiting pigment. It is an air Drying Primer, Red version contains natural Red Oxide.
It is recommended as primer on M.S. surface for General Industries, Fabrication Industries, Forging and Casting Industries, Agriculture euipment manufacturers, Heavy machineries, PEBs, Structural steel etc, where fast turn around is required. It can also be applied over hand prepared steel for use in mild industrial or commercial environment.
Colour
Redoxide, Yellow, White, Limited Shades
Finish
Eggshell (20-40 GU at 60° angle)
Soild by Volume
52 ± 3%
Supply Weight (Kg/ Ltr)
1.25±0.05
Flash Point
34° C
Dry Heat Resistance
Intermittent : 140°C, Continuous : 120°C
Shelf Life
12 months
Recommended film thickness per coat
Dry Film Thickness
30-50μ in single coat
Wet Film Thickness
60-95μ in single coat
Therotical Coverage Rate
17.25 sq.mt / lit at recommended DFT of 30μ
All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning. This product is suitable for use over phosphate washed steel.
Primed Surface : Already primed (or wash primed) surface should be dry and free from all contamination and Indoprotect 490 should be applied within the overcoating intervals specified in earlier primer/ etch primer TDS. Area of damaged primer or rework etc should be prepared as per specified standards, either by power tool cleaning or other means.
Wood : Clean and dry surface. Surface contamination is to be removed by detergents and fresh water cleaning.
Steel : Abrasive blast clean to a minimum of Sa2½ (ISO 8501-1:2007). Surface defects revealed by the blast cleaning process should be ground, filled, or treated in the appropriate manner. A surface profile of 30-40 microns is recommended.
Aluminium : The surface should be hand or machine abraded with non-metallic abrasives or bonded fibre machine or hand abrasive pads to impart a scratch pattern to the surface and to remove all polish from the surface. Else abrasive sweep blast to a standard similar to ISO 8501-1:2007 Sa1 to create a surface profile would be best method for surface prepration.
Application Method
Spray/ Airless Spray/Brush/ Roller
Mixing Ratio
One Component Coating
Thinner and Cleaner
Indokote Thinner (IK.1701/ IK.900)
Airless Nozzle Orifice
0.33 - 0.45mm
Nozzle Pressure
155 kg/cm² or 2200 psi