Indopoxy 320

/ Primers / Epoxy / Indopoxy 320

Epoxy

Epoxy Zinc Phosphate Rapid Recoat Primer

Indopoxy 320 is a Two component amine cured fast drying anti corrosive general industrial primer containing Zinc Phosphate as corrosion inhibiting pigments.

Recommended Use

It is recommended as undercoat on M.S. and concrete surface in diverse areas of use in Industries and maintenance projects. Indopoxy 320 is recommended for General & Heavy Fabrication industries, OEM components, Chemical and Pharmaceutical Industries, MS structures, PEBs due to its fast drying and abrasion resistance qualities. It can be overcoated within one hour of application at ambient temperature, hence making it ideal to be use in variety of applications.

  • Colour

    Grey & Custom Shades

  • Finish

    Matt

  • Soild by Volume

    45 ± 2%

  • Supply Weight (Kg/ Ltr)

    1.50±0.05

  • Flash Point

    29° C

  • Dry Heat Resistance

    Intermittent : 120°C, Continuous : 100°C

  • Shelf Life

    12 months

Film Thickness

Recommended film thickness per coat

  • Dry Film Thickness

    35-50μ in single coat

  • Wet Film Thickness

    75-110μ in single coat

  • Therotical Coverage Rate

    11.25 sq.mt / lit at recommended DFT of 40μ

All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.


Repair Cases : Corroded areas should be power tool cleaned to St3 or blast cleaned to Sa2 or better. Existing system should be dry and free from loose paint, salt, grease and other contaminants prior to overcoating.


New steel : Abrasive blasting to Sa 2½ (ISO 8501-1:2007). For temporary protection, if required, use a suitable shopprimer. All damage of shopprimer and contamination from storage and fabrication should be thoroughly cleaned prior to final painting.


Maintenance : Remove oil and grease etc. thoroughly with suitable detergent. Remove salts and other contaminants by high pressure fresh water cleaning. Clean damaged areas thoroughly by power tool cleaning to St 3 (ISO 8501-1:2007) (minor areas) or by abrasive blasting to min. Sa 2, preferably to Sa 2½ (ISO 8501-1:2007). Improved surface preparation will improve the performance of the product.


Stainless steel : To be abrasive blast cleaned to a uniform, sharp, dense profile (ISO Comparator Medium (G), corresponding to Rz minimum 50 micron. Any salts, grease, oil, etc. to be removed before abrasive blasting is commenced.

  • Application Method

    Spray/ Airless Spray/Brush/ Roller

  • Mixing Ratio

    4 Part (Base) : 1 Part (Hardener)

  • Pot Life

    Three Hours at 30°C

  • Thinner and Cleaner

    Indopoxy Epoxy Thinner (IK.1501)

  • Airless Nozzle Orifice

    0.38 - 0.53mm

  • Nozzle Pressure

    155 kg/cm² or 2200 psi