Indopoxy 630HB

/ Primers / Epoxy / Indopoxy 630HB

Epoxy

Epoxy High Solid High Build Zinc Phosphate Primer

Indopoxy 630HB is a Two component Polymide cured anti corrosive high performance primer containing Zinc Phosphate as corrosion inhibiting pigments.

Recommended Use

It is recommended as primer on M.S. surface in diverse areas of tank interiors, exteriors, pipelines, structural steel etc. It has also suitable for flow and dip application and provides excellent chemical and corrosion protection. Indopoxy 630HB is recommended for Thermal, Hydro Power Projects, Petrochemical, Transformers and Refineries due to its excellent corrosion and abrasion protection qualities.

  • Colour

    Grey

  • Finish

    Matt to Eggshell

  • Soild by Volume

    70 ± 3%

  • Supply Weight (Kg/ Ltr)

    1.65±0.05

  • Flash Point

    29° C

  • Dry Heat Resistance

    Intermittent : 120°C, Continuous : 100°C

  • Shelf Life

    12 months

Film Thickness

Recommended film thickness per coat

  • Dry Film Thickness

    60-100μ in single coat

  • Wet Film Thickness

    85-140μ in single coat

  • Therotical Coverage Rate

    10 sq.mt / lit at recommended DFT of 70μ

All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.


Repair Cases : Corroded areas should be power tool cleaned to St3 or blast cleaned to Sa2 or better. Existing system should be dry and free from loose paint, salt, grease and other contaminants prior to overcoating.


New steel : Abrasive blasting to Sa 2½ (ISO 8501-1:2007). For temporary protection, if required, use a suitable shopprimer. All damage of shopprimer and contamination from storage and fabrication should be thoroughly cleaned prior to final painting.


Maintenance : Remove oil and grease etc. thoroughly with suitable detergent. Remove salts and other contaminants by high pressure fresh water cleaning. Clean damaged areas thoroughly by power tool cleaning to St 3 (ISO 8501-1:2007) (minor areas) or by abrasive blasting to min. Sa 2, preferably to Sa 2½ (ISO 8501-1:2007). Improved surface preparation will improve the performance of the product.


Stainless steel : To be abrasive blast cleaned to a uniform, sharp, dense profile (ISO Comparator Medium (G), corresponding to Rz minimum 50 micron. Any salts, grease, oil, etc. to be removed before abrasive blasting is commenced.

  • Application Method

    Spray/ Airless Spray/Brush/ Roller

  • Mixing Ratio

    4 Part (Base) : 1 Part (Hardener)

  • Pot Life

    Three Hours at 30°C

  • Thinner and Cleaner

    Indopoxy Epoxy Thinner (IK.1501)

  • Airless Nozzle Orifice

    0.38 - 0.53mm

  • Nozzle Pressure

    155 kg/cm² or 2200 psi

quick inquiry