Two component highly Corrosion Protective (Polymide cured) coating, pigmented with Zinc Phosphate and Micaceous Iron Oxide. It provides a tough coating with long term protection. It has excellent adhesion and moisture barrier action for steel structures especially exposed to marine conditions.
It is recommended as undercoat and/ or Intermediate coat on Structures, Equipments, Pipe Lines, Vessels, Machinaries, Storage Tanks etc in Infrastructure projects, Bridges, Refinaries Pipelines, Chemical Plants, Steel Plants, Cement Plants, Petrochemicals Plants etc. This product is a High Performance coating, provides maximum protection in single coat as compare to any other Anti-corrosion System. It has also suitable for flow and dip application and provides excellent chemical and corrosion protection.
Colour
Grey
Finish
Eggshell to Semi Glossy
Soild by Volume
75 ± 2%
Supply Weight (Kg/ Ltr)
1.70±0.05
Flash Point
29° C
Dry Heat Resistance
Intermittent : 130°C, Continuous : 110°C
Shelf Life
12 months
Recommended film thickness per coat
Dry Film Thickness
75-150μ in single coat
Wet Film Thickness
100-200μ in single coat
Therotical Coverage Rate
10 sq.mt / lit at recommended DFT of 75μ
All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.
Repair Cases : Corroded areas should be power tool cleaned to St3 or blast cleaned to Sa2 or better. Existing system should be dry and free from loose paint, salt, grease and other contaminants prior to overcoating.
New steel : Abrasive blasting to Sa 2½ (ISO 8501-1:2007). For temporary protection, if required, use a suitable shopprimer. All damage of shopprimer and contamination from storage and fabrication should be thoroughly cleaned prior to final painting.
Maintenance : Remove oil and grease etc. thoroughly with suitable detergent. Remove salts and other contaminants by high pressure fresh water cleaning. Clean damaged areas thoroughly by power tool cleaning to St 3 (ISO 8501-1:2007) (minor areas) or by abrasive blasting to min. Sa 2, preferably to Sa 2½ (ISO 8501-1:2007). Improved surface preparation will improve the performance of the product.
Stainless steel : To be abrasive blast cleaned to a uniform, sharp, dense profile (ISO Comparator Medium (G), corresponding to Rz minimum 50 micron. Any salts, grease, oil, etc. to be removed before abrasive blasting is commenced.
Application Method
Spray/ Airless Spray/Brush/ Roller
Mixing Ratio
4 Part (Base) : 1 Part (Hardener)
Pot Life
Four Hours at 30°C
Thinner and Cleaner
Indopoxy Epoxy Thinner (IK.1501)
Airless Nozzle Orifice
0.45 - 0.58mm
Nozzle Pressure
176 kg/cm² or 2500 psi
Download Brochure