Two component EPOXY based Surface Tolerant (Polyamine cured) coating pigmented with specialized Anti Corrosion Pigments. It provides a tough coating with long term protection on manually cleaned steel or concrete surfaces and can be used as maintenance coatings in high build system.
690HSHB mastic is recommended as primer, intermediate coat or as topcoat on Structures, Equipments, Pipelines, Storage Tanks etc including hand prepared rusty steel, hydroblasted steel, and a wide range of intact, aged coatings in Infrastructure projects, Bridges, Refinaries Pipelines, Chemical Plants, Steel Plants, Cement Plants, Petrochemicals Plants etc. This product is a High Performance coating, provides excellent surface tolerance as compare to any other Anti-corrosion System.
Colour
Grey / Customized Limited Shades
Finish
Semi Glossy
Soild by Volume
80 ± 2%
Supply Weight (Kg/ Ltr)
1.55±0.05
Flash Point
33° C
Dry Heat Resistance
Intermittent : 120°C, Continuous : 100°C
Shelf Life
12 months
Recommended film thickness per coat
Dry Film Thickness
100-150μ in single coat
Wet Film Thickness
125-190μ in single coat
Therotical Coverage Rate
8 sq.mt / lit at recommended DFT of 100μ
All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.
Repair Cases : Corroded areas should be power tool cleaned to St3 or blast cleaned to Sa2 or better. Existing system should be dry and free from loose paint, salt, grease and other contaminants prior to overcoating.
New steel : Abrasive blasting to Sa 2½ (ISO 8501-1:2007). For temporary protection, if required, use a suitable shopprimer. All damage of shopprimer and contamination from storage and fabrication should be thoroughly cleaned prior to final painting.
Maintenance : Remove oil and grease etc. thoroughly with suitable detergent. Remove salts and other contaminants by high pressure fresh water cleaning. Clean damaged areas thoroughly by power tool cleaning to St 3 (ISO 8501-1:2007) (minor areas) or by abrasive blasting to min. Sa 2, preferably to Sa 2½ (ISO 8501-1:2007). Improved surface preparation will improve the performance of the product.
Aged Surface : Indopoxy 690HSHB is suitable for overcoating a limited range of intact, tightly adherent aged coatings. Loose or flaking coatings should be removed back to a firm edge. Glossy finishes require light abrasion by emery paper or power tool to provide a physical key.
Application Method
Spray/ Airless Spray/Brush/ Roller
Mixing Ratio
3 Part (Base) : 1 Part (Hardener)
Pot Life
Two Hours at 30°C
Thinner and Cleaner
Indopoxy Epoxy Thinner (IK.1501)
Airless Nozzle Orifice
0.45 - 0.58mm
Nozzle Pressure
176 kg/cm² or 2500 psi
Download Brochure