Indopoxy 710ZR

/ Primers / Epoxy / Indopoxy 710ZR

Epoxy

Epoxy High Performance Zinc Rich Primer

Two component high solid, metallic zinc rich epoxy primer to provide excellent corrosion resistance as single coat or as high performance coating system. It contains 90% zinc in dry film by weight. Highly suitable for carbon steel, repair of inorganic zinc silicate coating and damaged galvanised steel substrates.

Recommended Use

Indopoxy 710ZR is recommended as a high performance primer to give maximum protection as part of any anti-corrosive coating system for aggressive environments such as offshore environments, refineries, power plants, bridges, buildings, mining equipment etc. Indopoxy 710ZR showcase superior performance in adhesion and cathodic protection as compared to other zinc rich epoxy coatings.

  • Colour

    Grey

  • Finish

    Matt

  • Soild by Volume

    60 ± 3%

  • Supply Weight (Kg/ Ltr)

    2.80±0.05

  • Flash Point

    29° C

  • Dry Heat Resistance

    Intermittent : 180°C, Continuous : 130°C

  • Shelf Life

    12 months

Film Thickness

Recommended film thickness per coat

  • Dry Film Thickness

    50-75μ in single coat

  • Wet Film Thickness

    85-125μ in single coat

  • Therotical Coverage Rate

    10 sq.mt / lit at recommended DFT of 60μ

All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.


New steel : Abrasive blasting to Sa 2½ (ISO 8501-1:2007). For temporary protection, if required, use a suitable shopprimer. All damage of shopprimer and contamination from storage and fabrication should be thoroughly cleaned prior to final painting.


Shop Primed : Indopoxy 710ZR is suitable for application to steelwork freshly coated with zinc silicate shop primers ONLY. If the zinc silicate shop primer shows extensive or widely scattered breakdown, or excessive zinc corrosion, overall sweep blasting is a must. Other than zinc silicate shop primed surfaces are not suitable for overcoating and will require complete removal by abrasive blast cleaning.

  • Application Method

    Airless Spray/ Spray/ Brush/ Roller

  • Mixing Ratio

    3 Part (Base) : 1 Part (Hardener)

  • Pot Life

    Six Hours at 30°C

  • Thinner and Cleaner

    Indopoxy Epoxy Thinner (IK.1501)

  • Airless Nozzle Orifice

    0.43 - 0.53mm

  • Nozzle Pressure

    176 kg/cm² or 2500 psi