updraftplus domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/indoksf5/public_html/wp-includes/functions.php on line 6114Two component aliphatic Isocyanate cured Glossy, Fast Cured, DTM (Direct-to-Metal) polyurethane finish. Indothane 4800G is pigmented with zinc phosphate to provide anti corrosive properties.
Indothane 4800G is specially designed for use as a single coat primer cum finish coating system to protect Construction and Mining heavy machinery, Agricultural equipment, Transportation vehicles, material handling and lifting equipment, Tanks and Vessels, and industrial structures. It gives good adhesion properties over correctly prepared steel and stainless steel and provides Good gloss and colour retention.
Colour
Any IS/ RAL/ Custom Shades
Finish
Glossy (75-90 GU at 60° angle)
Soild by Volume
55 ± 2%
Supply Weight (Kg/ Ltr)
1.15±0.05
Flash Point
30° C
Dry Heat Resistance
Intermittent : 100°C, Continuous : 80°C
Shelf Life
12 months
Recommended film thickness per coat
Dry Film Thickness
50-80μ in single coat
Wet Film Thickness
90-145μ in single coat
Therotical Coverage Rate
11.00 sq.mt / lit at recommended DFT of 50μ
All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning. This product is suitable for use over phosphate washed steel.
Primed Surface: The primed surface should be dry and free from all contamination and Indothane 4800G should be applied within the overcoating intervals specified in primer TDS.
Area of damaged primer or rework etc should be prepared as per specified standards, either by power tool cleaning or other means.
Steel : Abrasive blast clean to a minimum of Sa2½ (ISO 8501-1:2007). Surface defects revealed by the blast cleaning process should be ground, filled, or treated in the appropriate manner. A surface profile of 30-40 microns is recommended.
Stainless Steel : Dirt and oils shoule be removed by solvent cleaning or other suitable cleaner followed by a thorough water rinsing. Sand or abrasive sweep blast to a standard similar to ISO 8501-1:2007 Sa1 to create a surface profile.
Application Method
Spray/ Airless Spray/Brush/ Roller
Mixing Ratio
4 Part (Base) : 1 Part (Hardener)
Pot Life
Three Hours at 30°C
Thinner and Cleaner
Indothane PU Thinner (IK.1705)
Airless Nozzle Orifice
0.33 - 0.45mm
Nozzle Pressure
155 kg/cm² or 2200 psi