Two component aliphatic Isocyanate cured high solid, Glossy, DTM (Direct-to-Metal) acrylic polyurethane primer cum finish coating. Indothane 2075G is also pigmented with zinc phosphate to provide anti corrosive properties.
Indothane 2075G is specially designed for use as a single or two coat primer/finish coating system to protect Construction and Mining heavy machinery, Agricultural equipment, Transportation vehicles, material handling and lifting equipment, Tanks and Vessels, pumps, valves and other small motors and machinery. Indothane 2075G is particularly suited for use as a rapid drying system for fast handling times and maximising the production throughput. It gives good adhesion properties over correctly prepared steel, galvanised steel and stainless steel and provides Good gloss and colour retention.
Colour
Any IS/ RAL/ Custom Shades
Finish
Glossy (80-95 GU at 60° angle)
Soild by Volume
60 ± 2%
Supply Weight (Kg/ Ltr)
1.20±0.05
Flash Point
33° C
Dry Heat Resistance
Intermittent : 120°C, Continuous : 100°C
Shelf Life
12 months
Recommended film thickness per coat
Dry Film Thickness
50-100μ in single coat
Wet Film Thickness
85-160μ in single coat
Therotical Coverage Rate
12.00 sq.mt / lit at recommended DFT of 50μ
All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning. This product is suitable for use over phosphate washed steel.
Primed Surface : The primed surface should be dry and free from all contamination and Indothane 2075G should be applied within the overcoating intervals specified in primer TDS.
Area of damaged primer or rework etc should be prepared as per specified standards, either by power tool cleaning or other means.
steel : Abrasive blast clean to a minimum of Sa2½ (ISO 8501-1:2007). Surface defects revealed by the blast cleaning process should be ground, filled, or treated in the appropriate manner. A surface profile of 30-40 microns is recommended.
Stainless Steel, Galvanised Steel and Aluminium : Dirt and oils shoule be removed by solvent cleaning or other suitable cleaner followed by a thorough water rinsing. Sand or abrasive sweep blast to a standard similar to ISO 8501-1:2007 Sa1 to create a surface profile.
Application Method
Spray/ Airless Spray/Brush/ Roller
Mixing Ratio
4 Part (Base) : 1 Part (Hardener)
Pot Life
Three Hours at 30°C
Thinner and Cleaner
Indothane PU Thinner (IK.1705)
Airless Nozzle Orifice
0.33 - 0.45mm
Nozzle Pressure
155 kg/cm² or 2200 psi