Two component EPOXY based Polymide cured chemical resistance Top coating. This product exhibits good abrasion resistance and good protection agianst spills or spilage of range of corrosive chemicals, solvents, Acids and Alkalis, renders durable finish in industrial and marine environment.
It is recommended as tough, hard wearing coating on properly primed surface. It is recommended as universal epoxy topcoat in general industries for Structures, Concrete, Equipments, Machinaries, Storage Tanks etc. This product is recommended in Power Plants, Transmission lines, Infrastructure projects, Bridges, Chemical Plants, Food & Pharmaceutical Plants, Mining & Steel Plants, Petrochemicals Plants etc.
Colour
Any IS/ RAL/ Custom Shades
Finish
Glossy (70-85GU at 60° angle)
Soild by Volume
52 ± 2%
Supply Weight (Kg/ Ltr)
1.35±0.05
Flash Point
26° C
Dry Heat Resistance
Intermittent : 120°C, Continuous : 100°C
Shelf Life
12 months
Recommended film thickness per coat
Dry Film Thickness
40-60μ in single coat
Wet Film Thickness
80-120μ in single coat
Therotical Coverage Rate
12.50 sq.mt / lit at recommended DFT of 40μ
All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.
Primed Surface : The primed surface should be dry and free from all contamination and Indopoxy 5070 should be applied within the overcoating intervals specified in primer TDS. Area of damaged primer or rework etc should be prepared as per specified standards, either by power tool cleaning or other means.
Maintenance : Remove oil and grease, salts and other contaminants by high pressure fresh water cleaning. Clean damaged areas thoroughly by power tool cleaning to St 3 (ISO 8501-1:2007) (minor areas) or by abrasive blasting to min. Sa 2, preferably to Sa 2½ (ISO 8501-1:2007). A patch primer should be applied before application of Indopoxy 5070 for desired performance of the product.
Concrete : Indopoxy 5070 is suitable to apply over concrete surfaces. Concrete should be cured for a minimum of 30 days prior to coating. The moisture content of the concrete should be below 5%. All surfaces should be clean, dry and free from curing compounds, release agents, trowelling compounds, surface hardeners, efflorescence, grease, oil, dirt, old coatings. All poured and precast concrete must also be sweep blasted (preferred) or acid etched to remove laitence. Priming should be carried out using Indopoxy 5070HB or Indopoxy 5070 at low viscosity to fill pores surface before final coating.
Application Method
Conventional Spray/ Airless Spray/Brush/ Roller
Mixing Ratio
4 Part (Base) : 1 Part (Hardener)
Pot Life
Three Hours at 30°C
Thinner and Cleaner
Indothane Epoxy Thinner (IK.1501)
Airless Nozzle Orifice
0.38 - 0.53mm
Nozzle Pressure
176 kg/cm² or 2500 psi