A high solid, high build, high performance, two component epoxy finish with excellent chemical and abrasion resistance. This product has excellent performance when exposed to chemical/ industrial environment.
Indopoxy 5080HS can be used as finish coat or as single coat system in atmospheric environments or as a final coat in immersed environment. Highly recommended as topcoat in high performance coating system in atmospheric and immersed environments. Suitable for Structures, Concrete, Equipments, Machineries, Storage Tanks etc in Nuclear and other Power Plants, Infrastructure projects, Bridges, Chemical Plants, Food & Pharmaceutical Plants, Mining & Steel Plants, Petrochemicals Plants etc.
Colour
Any IS/ RAL/ Custom Shades
Finish
Glossy (70-85GU at 60° angle)
Soild by Volume
75 ± 2%
Supply Weight (Kg/ Ltr)
1.40±0.05
Flash Point
28° C
Dry Heat Resistance
Intermittent : 130°C, Continuous : 100°C
Shelf Life
12 months
Recommended film thickness per coat
Dry Film Thickness
60-120μ in single coat
Wet Film Thickness
80-160μ in single coat
Therotical Coverage Rate
12.50 sq.mt / lit at recommended DFT of 60μ
All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.
Primed Surface : The primed surface should be dry and free from all contamination and Indopoxy 5080HS should be applied within the overcoating intervals specified in primer TDS. Area of damaged primer or rework etc should be prepared as per specified standards, either by power tool cleaning or other means.
Maintenance : Remove oil and grease, salts and other contaminants by high pressure fresh water cleaning. Clean damaged areas thoroughly by power tool cleaning to St 3 (ISO 8501-1:2007) (minor areas) or by abrasive blasting to min. Sa 2, preferably to Sa 2½ (ISO 8501-1:2007).
Stainless Steel, Galvanised Steel and Aluminium : The surface should be hand or machine abraded with non-metallic abrasives or bonded fibre machine or hand abrasive pads to impart a scratchpattern to the surface and all polish should be removed from the surface. Else Sand or abrasive sweep blast to a standard similar to ISO 8501-1:2007 Sa1 to create a surface profile.
Concrete : Indopoxy 5080HS is suitable to apply over concrete surfaces. Concrete should be cured for a minimum of 30 days prior to coating. The moisture content of the concrete should be below 5%. All surfaces should be clean, dry and free from curing compounds, release agents, trowelling compounds, surface hardeners, efflorescence, grease, oil, dirt, old coatings. All poured and precast concrete must also be sweep blasted (preferred) or acid etched to remove laitence.
Application Method
Conventional Spray/ Airless Spray/Brush/ Roller
Mixing Ratio
4 Part (Base) : 1 Part (Hardener)
Pot Life
Three Hours at 30°C
Thinner and Cleaner
Indothane Epoxy Thinner (IK.1501)
Airless Nozzle Orifice
0.43 - 0.58mm
Nozzle Pressure
150 kg/cm² or 2100 psi
Download Brochure